優(yōu)勢：
|
Item |
Unit |
Value |
Test Standard |
||
|
Thickness |
um |
50±5 |
ASTM D374 |
||
|
Color |
/ |
Translucent |
Visual |
||
|
UV Curing Parameter |
|
365nm @70mW for 60 secs |
SG Method |
||
|
Open time after UV* |
Hours |
8 |
SG Method |
||
|
Final bonding time (at RT) |
Hours |
48 |
SG Method |
||
|
Final bonding time (at 70C) |
Hours |
3 |
SG Method |
||
|
Glass transition temperature (after UV curing) |
oC |
66 |
DMA |
||
|
180o Peel adhesion strength (SUS) |
Before UV curing |
N/inch |
13 |
ASTM D3330 |
|
|
After UV curing |
33 |
||||
|
Dynamic shear strength (SUS/SUS) |
MPa |
>15 |
ASTM D1002 |
||
|
Modulus (at ~23C) |
Before UV curing |
MPa |
0.12 |
DMA |
|
|
After UV curing |
MPa |
1478 |
DMA |
||